POLYETHYLENE-LDPE
PRODUCT DATA SHEET
POLYETHYLENE | LDPE | 2047 – 37
| Product Category |
|---|
|
POPOLYMER |
| Product Name |
|---|
|
POLYETHYLENE – LDPE |
| Grade |
|---|
|
2102047 – 37 |
| Property | Value | Unit | Test Method |
|---|---|---|---|
|
Physical Properties |
|
|
ISO1133 |
|
MFI (190 0C /2 .16 Kg ) |
4.7 |
dg/min |
ISO 1183 (A) |
|
Density |
920 |
Kg/m3 |
|
|
Impact strength |
15 |
KJ/m |
ASTM D 4272 |
|
Tear strength (TD) |
25 |
KN/m |
ISO 6383-2 |
|
Tear Strength (MD) |
80 |
KN/m |
ISO 6383-2 |
|
Yield stress (TD) |
11 |
MPa |
ISO 527 |
|
Yield stress (MD) |
12 |
MPa |
ISO 527 |
|
Tensile Stress at break (TD) |
15 |
MPa |
ISO 527 |
|
Tensile Stress at break (MD) |
27 |
MPa |
ISO 527 |
|
Strain at Break (TD) |
>500 |
% |
ISO 527 |
|
Strain at Break (MD) |
100 |
% |
ISO 527 |
|
Modulus of Elasticity (TD) |
200 |
MPa |
ISO 527 |
|
Modulus of Elasticity (MD) |
200 |
MPa |
ISO 527 |
|
Coefficient of friction |
0.2 |
|
ASTM D 1894 |
|
Blocking |
20 |
g |
SABTEC method |
|
Re-blocking |
10 |
g |
SABTEC method |
|
Haze |
9 |
% |
ASTM D 1003A |
|
Gloss(45o) |
55 |
% |
ASTM D 2457 |
|
Clarity |
21 |
mV |
|
| Application |
|---|
|
2047/37 intended for very thin film, requiring very good optical properties and thus very suitable for laundry and textile packaging. |
| Packaging |
|---|
|
25 Kg plastic bag |
PRODUCT DATA SHEET
POLYETHYLENE | LDPE | 2100TN00
| Product Category |
|---|
|
POPOLYMER |
| Product Name |
|---|
|
POLYETHYLENE – LDPE |
| Grade |
|---|
|
2100TN00 |
| Property | Test Method | Unit | Value |
|---|---|---|---|
|
MFI (200 o c/5kg ) |
ISO 1133 |
g/10 min |
0.3 |
|
Density |
ISO 1183 (A) |
Kg/m3 |
921 |
|
Haze |
ASTM D 1003 (A) |
% |
15 |
|
Clarity |
DSM Method |
mV |
56 |
|
Gloss |
ASTM D2457 |
% |
39±5 |
|
Anti Oxidant |
DSM Method |
ppm |
600±60 |
|
Anti Block |
|
ppm |
|
|
Slip |
|
ppm |
|
|
Impact Strength |
ASTM D4272 |
kJ/m |
35 |
|
Tear strength TD |
ISO 6383-2 |
KN/m |
25 |
|
Tear strength MD |
ISO 6383-2 |
KN/m |
20 |
|
Yield Stress TD |
ISO R527-1 |
MPa |
11 |
|
Yield Stress MD |
ISO R527-1 |
MPa |
12 |
|
Tensile strength TD |
ISO R527-1 |
MPa |
26 |
|
Tensile strength MD |
ISO R527-1 |
MPa |
29 |
|
Elongation @ break TD |
ISO R527-1 |
% |
>500 |
|
Elongation @ break MD |
ISO R527-1 |
% |
>200 |
|
Modulus of elasticity TD |
ISO R527-1 |
MPa |
190 |
|
Modulus of elasticity MD |
ISO R527-1 |
MPa |
180 |
|
Co efficient of friction |
ASTM D1894 |
– |
0.7 |
| Application |
|---|
|
It is suitable for application in Shrink hoods, Industrial sacks, Heavy duty, carrier bags and liners. |
| Packaging |
|---|
|
25 Kg plastic bag |
POLYETHYLENE-LDPE
PRODUCT DATA SHEET
POLYETHYLENE | LDPE | 2102TX00
| Product Category |
|---|
|
POLYMER |
| Product Name |
|---|
|
POLYETHYLENE – LDPE |
| Grade |
|---|
|
2102TX00 |
| Property | Test Method | Unit | Value |
|---|---|---|---|
|
MFI |
ISO 1133 |
g/10 min |
1.9 |
|
Density |
ISO 1183 (A) |
Kg/m3 |
921 |
|
Haze |
ASTM D 1003 (A) |
% |
11 |
|
Clarity |
DSM Method |
mV |
29 |
|
Gloss |
ASTM D2457 |
% |
50±5 |
|
Anti Oxidant |
DSM Method |
ppm |
600±60 |
|
Anti Block |
– |
ppm |
– |
|
Slip |
– |
ppm |
– |
|
Impact Strength |
ASTM D4272 |
kJ/m |
26 |
|
Tear strength TD |
ISO 6383-2 |
KN/m |
25 |
|
Tear strength MD |
ISO 6383-2 |
KN/m |
60 |
|
Yield Stress TD |
ISO R527-1 |
MPa |
11 |
|
Yield Stress MD |
ISO R527-1 |
MPa |
13 |
|
Tensile strength TD |
ISO R527-1 |
MPa |
20 |
|
Tensile strength MD |
ISO R527-1 |
MPa |
– |
|
Elongation @ break TD |
ISO R527-1 |
% |
>500 |
|
Elongation @ break MD |
ISO R527-1 |
% |
>150 |
|
Modulus of elasticity TD |
ISO R527-1 |
MPa |
200 |
|
Modulus of elasticity MD |
ISO R527-1 |
MPa |
190 |
|
Co efficient of friction |
ASTM D1894 |
– |
>1.0 |
| Application |
|---|
|
It is used in wide range of widths and thicknesses e.g. for punches, bags, liners and lamination film. |
| Packaging |
|---|
|
25 Kg plastic bag |
PRODUCT DATA SHEET
POLYETHYLENE | LDPE | 2119
| Product Category |
|---|
|
POLYMER |
| Product Name |
|---|
|
POLYETHYLENE – LDPE |
| Grade |
|---|
|
2119 |
| Property | Value | Unit | Test Method |
|---|---|---|---|
|
MFI(190 0C /2 .16 Kg ) |
1.9 |
dg/min |
ISO1133 |
|
Density |
921 |
Kg/m3 |
ISO 1183 (A) |
|
Impact strength |
26 |
KJ/m |
ASTM D 4272 |
|
Tear strength (TD) |
25 |
KN/m |
ISO 6383-2 |
|
Tear Strength (MD) |
60 |
KN/m |
ISO 6383-2 |
|
Yield stress (TD) |
11 |
MPa |
ISO 527 |
|
Yield stress (MD) |
13 |
MPa |
ISO 527 |
|
Tensile stress at break (TD) |
20 |
MPa |
ISO 527 |
|
Tensile stress at break (MD) |
35 |
MPa |
ISO 527 |
|
Strain at Break (TD) |
>500 |
% |
ISO 527 |
|
Strain at Break (MD) |
>150 |
% |
ISO 527 |
|
Modulus of Elasticity (TD) |
200 |
MPa |
ISO 527 |
|
Modulus of Elasticity (MD) |
190 |
MPa |
ISO 527 |
|
Coefficient of friction |
>1 |
– |
ASTM D 1894 |
|
Blocking |
20 |
g |
SABTEC method |
|
Re-blocking |
100 |
g |
SABTEC method |
|
Haze |
9 |
% |
ASTM D 1003A |
|
Gloss (45o) |
55 |
% |
ASTM D 2457 |
|
Clarity |
26 |
mV |
– |
| Application |
|---|
|
2119 is suitable for general purpose film and for lamination. |
| Packaging |
|---|
|
25 Kg plastic bag |
PRODUCT DATA SHEET
POLYETHYLENE | LDPE | 2420 H
| Product Category |
|---|
|
POPOLYMER |
| Product Name |
|---|
|
POLYETHYLENE – LDPE |
| Grade |
|---|
|
2420 H |
| Property | Value | Unit | Test Method |
|---|---|---|---|
|
Mass Density (23 °C) |
0.924 |
g/cm3 |
ISO1183 |
|
Melt Flow Rate (190°C /2.16kg) |
2 |
g/10min |
ISO1133 |
|
Melting point |
112 |
°C |
ISO11357 |
|
Vicat softening temperature, A/50 |
95 |
°C |
ISO306 |
|
Tensile Modulus of Elasticity |
270 |
MPa |
ISO527 |
|
Stress at Yield |
11 |
MPa |
ISO527 |
|
Shore D hardness |
48 |
– |
ISO868 |
|
Max. tensile strength MD |
23 |
MPa |
ISO527 |
|
Max. tensile strength TD |
21 |
MPa |
ISO527 |
|
Maximum elongation MD |
580 |
% |
ISO527 |
|
Maximum elongation TD |
700 |
% |
ISO527 |
|
Dart Drop Impact |
110 |
g |
ASTM D1709 |
|
Gloss ( 60°) |
120 |
– |
ASTM D2457 |
|
Haze (40μm film) |
6.5 |
% |
ASTM D1003 |
| Application |
|---|
|
Blown film – Fine shrink film – Food packaging FFS film and bags – Packaging film for sanitary articles – Freezer film – Lamination film – Surface protection film – Sealing layer-Injection Molding •Foamed Products •Blow molding |
| Packaging |
|---|
|
25 Kg plastic bag |
PRODUCT DATA SHEET
POLYETHYLENE | HDPE | 2420D
| Product Category |
|---|
|
POPOLYMER |
| Product Name |
|---|
|
POLYETHYLENE – LDPE |
| Grade |
|---|
|
2420D |
| Property | Value | Unit | Test Method |
|---|---|---|---|
|
MFI(190 0C /2 .16 Kg ) |
0.25 |
g/cm3 |
ISO1133 |
|
Mass Density (23 DC) |
0.923 |
Kg/m3 |
ISO 1183 |
|
Melting point |
113 |
°C |
ISO11357 |
|
Vicat softening temperature, A/50 |
95 |
°C |
ISO306 |
|
Tensile Modulus of Elasticity |
260 |
MPa |
ISO527 |
|
Stress at Yield |
10 |
MPa |
ISO527 |
|
Shore D hardness |
48 |
– |
ISO868 |
|
Max. tensile strength MD |
25 |
MPa |
ISO527 |
|
Max. tensile strength TD |
24 |
MPa |
ISO527 |
|
Maximum elongation MD |
600 |
% |
ISO527 |
|
Maximum elongation TD |
650 |
% |
ISO527 |
|
Dart Drop Impact |
270 |
g |
ASTM D1709 |
|
Gloss ( 60°) |
100 |
– |
ASTM D2457 |
|
Haze (40μm film) |
8.5 |
% |
ASTM D1003 |
| Application |
|---|
|
Blown film – Heavy duty bags – In liners – Refuse sacks and bags -Carrier bags – Agricultural film – Building and construction film – Heavy duty shrink film-Blow molding articles -Extruding dip tube for spray valve – Steel pipe coating. |
| Packaging |
|---|
|
25 Kg plastic bag |
PRODUCT DATA SHEET
POLYETHYLENE | LDPE | LH0075
| Product Category |
|---|
|
POPOLYMER |
| Product Name |
|---|
|
POLYETHYLENE – LDPE |
| Grade |
|---|
|
LH0075 |
| Property | Test Method | Unit | Value |
|---|---|---|---|
|
MFI (190 C/2. 16 kg) |
ASTM D 1238 |
gr/10 min |
0.75 |
|
Density |
ASTM 209 B |
gr/ml |
0.921 |
|
Vicat softening point |
ASTM D 1525 |
C |
94 |
|
Elongation @ break (MD) |
ASTM D882 |
% |
300 min. |
|
Elongation @ break (TD) |
ASTM D 882 |
% |
450 min. |
|
Tensile @ break (MD) |
ASTM D 882 |
kg/cm2 |
170 min |
|
HDT |
ASTM D 648 |
oC |
33 |
|
Dart impact |
ASTM D 1709 |
gr |
120 min |
| Application |
|---|
|
Carrier bags -Shrink film-Industrial film -Dust bin liners -large bottles -Blow moulding of small containers -Packaging of pharmaceutical products |
| Packaging |
|---|
|
25 Kg plastic bag |