POLYETHYLENE-HDPE
PRODUCT DATA SHEET
POLYETHYLENE | HDPE | 52518
| Product Category |
|---|
|
POPOLYMER |
| Product Name |
|---|
|
POLYETHYLENE – HDPE |
| Grade |
|---|
|
52518 |
| Property | Unit | Value | Test Method |
|---|---|---|---|
|
Density |
(g/ml) |
0.952 |
ASTM D 1505 |
|
MFR(190°C/2.16kg) |
(g/10min) |
18 |
ASTM D 1238 |
|
Flexural modulus |
(MPa) |
1350 |
ASTM D 790 |
|
Notched Izod impact at 23°C |
(J/m) |
25 |
ASTM D 256/A |
|
Vicat softening point |
(°C) |
122 |
ASTM D 1525 |
| Application |
|---|
|
House wares, high fluidity – Injection molding grade |
| Packaging |
|---|
|
25 Kg plastic bag |
PRODUCT DATA SHEET
POLYETHYLENE | HDPE | BL3
| Product Category |
|---|
|
POLYMER |
| Product Name |
|---|
|
POLYETHYLENE – HDPE |
| Grade |
|---|
|
BL3 |
| Property | Test Method | Unit | Value |
|---|---|---|---|
|
Mass density (230C) |
ISO 1183 |
g/cm3 |
0.954 |
|
Melt Flow Rate (1900C/5.0kg) |
ISO 1133 |
g/10min |
1.2 |
|
Melt Flow Rate (1900C/21.6 kg) |
ISO 1133 |
g/10min |
23 |
|
Stress at Yield |
ISO 527 |
MPa |
26 |
|
Flexural Creep Modulus (4point,1min) |
DIN 19537-2 |
MPa |
1300 |
|
Tensile Modulus (230C, v = 1mm / min ,Secant) |
ISO 527 |
MPa |
1250 |
|
Stress at Break |
ISO 527 |
32 |
|
|
Elongation at Break |
ISO 527 |
% |
>600 |
|
Elongation at yield |
ISO 527 |
% |
10 |
|
Softening Temperature |
ISO 306 |
0C |
77 |
|
Brittle Temperature |
ASTM D746-72 |
0C |
< – 80 |
|
Shore D hardness |
ISO 868 |
– |
62 |
|
ESCR in Full Notch Creep Test (800C, 2% Arcopal h@3.5 MPa |
ISO CD 16770 |
|
|
|
Impact strength (230C) |
ISO 179/1eA |
Kj/m2 |
10 |
|
Swell ratio |
Internal |
% |
120 |
| Application |
|---|
|
Small blow moulding-Bottles-Containers (up to 5 litre )-Packing of pharmaceuticals & surfactants. |
| Packaging |
|---|
|
25 Kg plastic bag |
PRODUCT DATA SHEET
POLYETHYLENE | HDPE | EX3
| Product Category |
|---|
|
POLYMER |
| Product Name |
|---|
|
POLYETHYLENE – HDPE |
| Grade |
|---|
|
EX3 |
| Property | Unit | Typical Value | Test Method |
|---|---|---|---|
|
Mass density (230 C) |
g/cm3 |
0.956 |
ISO 1183 |
|
Melt Flow Rate (1900C/5.0kg) |
g/10min |
3.3 |
ISO 1183 |
|
Melt Flow Rate (1900C/21.6kg) |
g/10min |
33 |
ISO 1183 |
|
Stress at Yield |
MPa |
27 |
ISO 527 |
|
Flexural Creep Modulus (4point, 1min) |
MPa |
1350 |
DIN 19537-2 |
|
Tensile Modulus (230 C, v = 1mm / min ,Secant) |
MPa |
ISO 527 |
|
|
Stress at Break |
MPa |
31 |
ISO 527 |
|
Elongation at Break |
% |
>1000 |
ISO 527 |
|
Elongation at yield |
% |
10 |
ISO 527 |
|
Softening Temperature |
0C |
8 |
ISO 306 |
|
Brittle Temperature |
0C |
< – 80 |
ASTM D746-72 |
|
Shore D hardness |
– |
62 |
ISO 868 |
|
ESCR in Full Notch Creep Test (800C, 2% Arcopal ) |
h@2.5 MPa |
2 |
ISO CD 16770 |
|
Impact strength (230C) |
Kj/m2 |
23 |
ISO 179/1eA |
| Application |
|---|
|
Monofilaments, Ropes, Yarns- fish netting geotextiles & cavil engineering |
| Packaging |
|---|
|
25 Kg plastic bag |
PRODUCT DATA SHEET
POLYETHYLENE | HDPE | EX5
| Product Category |
|---|
|
POLYMER |
| Product Name |
|---|
|
POLYETHYLENE – HDPE |
| Grade |
|---|
|
EX5 |
| Property | Unit | Value | Test Method |
|---|---|---|---|
|
Mass density (230 C) |
ISO 1183 |
g/cm3 |
0.949 |
|
Melt Flow Rate (1900C/5.0kg) |
ISO 1133 |
g/10min |
0.28 |
|
Melt Flow Rate (1900C/21.6kg) |
ISO 1133 |
g/10min |
8 |
|
Stress at Yield |
ISO 527 |
MPa |
24 |
|
Stress at Break |
ISO 527 |
MPa |
35 |
|
Softening Temperature |
ISO 306 |
0C |
75 |
|
Brittle Temperature |
ASTM D746-72 |
0C |
< – 80 |
|
Shore D hardness |
ISO 868 |
– |
60 |
|
Max. tensile strength MD / TD |
ISO 527 |
MPa |
45/40 |
|
Tear strength MD / TD |
ISO 6383-2 |
m N |
200/450 |
|
Max. elongation MD / TD |
ISO 527 |
% |
400/450 |
|
Dart Drop Impact |
ASTM D 1709 |
g |
220 |
| Application |
|---|
|
Film extrusion-Counter bag, carrier bag -Wrapping films |
| Packaging |
|---|
|
25 Kg plastic bag |
PRODUCT DATA SHEET
POLYETHYLENE | HDPE | HB – 0035
| Product Category |
|---|
|
POLYMER |
| Product Name |
|---|
|
POLYETHYLENE – HDPE |
| Grade |
|---|
|
HB – 0035 |
| Property | Test Method | Unit | Value |
|---|---|---|---|
|
Mass density (230 C) |
ASTM D 1505 |
g/cm3 |
0.959 |
|
Melt Flow Rate (1900 C/2.16 kg) |
ASTM D1238 |
g/10min |
0.35 |
|
Izod impact strength |
ASTM D 256 |
Kg.cm/cm |
25 min |
|
Yellow index |
ASTM D 1925 |
– |
-5 max |
|
Ash content |
ASTM D 1063 |
wt% |
0.06 max |
|
Volatile matter |
ASTM D 1960 |
wt% |
0.05 max |
|
Tensile strength @ break |
ASTM D 638 |
gr/cm2 |
290 min |
|
Elongation @ break |
ASTM D 638 |
% |
900 min |
|
Melting point |
ASTM D 2117 |
oC |
130 |
|
Vicat softening point |
ASTM D 1525 |
oC |
126 |
|
ESCR |
ASTM D 1693 |
hr |
15 |
| Application |
|---|
|
•Small blow moulding •Bottles •Containers (up to 5 lit ) |
| Packaging |
|---|
|
25 Kg plastic bag |
PRODUCT DATA SHEET
POLYETHYLENE | HDPE | PE – 80
| Product Category |
|---|
|
POLYMER |
| Product Name |
|---|
|
POLYETHYLENE – HDPE |
| Grade |
|---|
|
PE 80 |
| Property | Test Method | Unit | Value |
|---|---|---|---|
|
Mass density (230C) |
ISO 1183 |
g/cm3 |
0.945 |
|
Melt Flow Rate (1900C/5.0kg) |
ISO 1133 |
g/10min |
0.45 |
|
Melt Flow Rate (1900 C/21.6 kg) |
ISO 1133 |
g/10min |
12 |
|
Stress at Yield |
ISO 527 |
MPa |
22 |
|
Flexural Creep Modulus (4point, 1min) |
DIN 19537-2 |
MPa |
950 |
|
Tensile Modulus (230C, v = 1mm / min ,Secant) |
ISO 527 |
MPa |
850 |
|
Stress at Break |
ISO 527 |
MPa |
35 |
|
Elongation at Break |
ISO 527 |
% |
>850 |
|
Elongation at yield |
ISO 527 |
% |
8 |
|
Softening Temperature |
ISO 306 |
0 C |
67 |
|
Brittle Temperature |
ASTM D746-72 |
0 C |
< – 80 |
|
Shore D hardness |
ISO 868 |
– |
60 |
|
ESCR in Full Notch Creep Test (800 C, 2% Arcopal ) |
ISO CD 16770 |
h@4.0 MPa |
50 |
|
Impact strength (230 C) |
ISO 179/1eA |
Kj/m2 |
23 |
|
Expected Properties on Application |
|||
|
S4 Test (RCP) |
ISO DIS 13477 |
Bar |
Pc> 3 |
|
Notch Test (SCG) |
ISO DIS 13479 |
h@4.0 MPa |
>250 |
|
Hydrostatic strength test (800 C) |
ISO 1167 |
h@4.6 MPa |
>1000 |
| Application |
|---|
|
Pipe extrusion PE 80 class -Industrial and pressure pipe , Gas pipe, drinking water pipe -Pressure less pipe , relining , fittings |
| Packaging |
|---|
|
25 Kg plastic bag |
PRODUCT DATA SHEET
POLYETHYLENE | HDPE | PE – 100
| Product Category |
|---|
|
POLYMER |
| Product Name |
|---|
|
POLYETHYLENE – HDPE |
| Grade |
|---|
|
PE 100 |
| Property | Test Method | Unit | Value |
|---|---|---|---|
|
Mass density (230C) |
ISO 1183 |
g/cm3 |
0.94 |
|
Melt Flow Rate (1900C/5.0kg) |
ISO 1133 |
g/10min |
0.22 |
|
Melt Flow Rate (1900C/21.6 kg) |
ISO 1133 |
g/10min |
6.2 |
|
Stress at Yield |
ISO 527 |
MPa |
23 |
|
Flexural Creep Modulus (4point, 1min) |
DIN 19537-2 |
MPa |
1050 |
|
Tensile Modulus (230C, v = 1mm / min ,Secant) |
ISO 527 |
MPa |
850 |
|
Stress at Break |
ISO 527 |
MPa |
36 |
|
Elongation at Break |
ISO 527 |
% |
>1000 |
|
Elongation at yield |
ISO 527 |
% |
10 |
|
Softening Temperature |
ISO 306 |
0C |
74 |
|
Brittle Temperature |
ASTM D746-72 |
0C |
< – 80 |
|
Shore D hardness |
ISO 868 |
|
62 |
|
ESCR in Full Notch Creep Test (800C, 2% rcopal ) |
ISO CD 16770 |
h@4.0 MPa |
400 |
|
Impact strength (230C) |
ISO 179/1eA |
Kj/m2 |
25 |
|
S4 Test (RCP) |
ISO DIS 13477 |
Bar |
Pc> 20 |
|
Notch Test (SCG) |
ISO DIS 13479 |
h@4.6 MPa |
>1000 |
|
Hydrostatic strength test (800c) |
ISO 1167 |
h@4.6 MPa |
>15000 |
| Application |
|---|
|
Pipe extrusion PE 100 class -Industrial and pressure pipe , Gas pipe, drinking water pipe -relining , fittings |
| Packaging |
|---|
|
25 Kg plastic bag |