POLYETHYLENE-LLDPE
PRODUCT DATA SHEET
POLYETHYLENE | LLDPE | LL 0209 AA
| Product Category |
|---|
|
POPOLYMER |
| Product Name |
|---|
|
POLYETHYLENE – LLDPE |
| Grade |
|---|
|
LL 0209 AA |
| Property | Test Method | Unit | Value |
|---|---|---|---|
|
MFI@190° C, 2.16 kg |
D1238 |
gr/10min |
0.9 |
|
Density |
D2839 |
gr/ml |
0.92 |
|
Vicat Softening Point |
D1525 |
°C |
100 |
|
Tensile Strength @Yield, MD/TD |
D638 |
Mpa |
10.5/11 |
|
Elongation @ Break, MD/TD |
D638 |
% |
620/840 |
|
Tensile Strength @ Break, MD/TD |
D688 |
Mpa |
41/32 |
|
Tear Strength, MD/TD |
D1922 |
gr/25mic |
145/370 |
|
Impact Strength, Dart |
D1709 |
gr |
150 |
|
Haze |
D1003 |
% |
10 |
|
Gloss (45°) |
D2457 |
Rating |
56 |
| Application |
|---|
|
It is suitable for application in Shrink hoods, Industrial sacks, Heavy duty, carrier bags and liners |
| Packaging |
|---|
|
25 Kg plastic bag |
PRODUCT DATA SHEET
POLYETHYLENE | LLDPE | LL0209 KJ
| Product Category |
|---|
|
POPOLYMER |
| Product Name |
|---|
|
POLYETHYLENE – LLDPE |
| Grade |
|---|
|
LL0209 KJ |
| Property | Test Method | Unit | Value |
|---|---|---|---|
|
MFI@190° C, 2.16 kg |
D1238 |
gr/10min |
0.9 |
|
Density |
D2839 |
gr/ml |
0.92 |
|
Vicat Softening Point |
D1525 |
°C |
100 |
|
Tensile Strength @ Yield, MD/TD |
D638 |
Mpa |
10.5/11 |
|
Elongation @ Break, MD/TD |
D638 |
% |
620/840 |
|
Tensile Strength @ Break, MD/TD |
D688 |
Mpa |
41/32 |
|
Tear Strength, MD/TD |
D1922 |
gr/25mic |
145/370 |
|
Impact Strength, Dart |
D1709 |
gr |
150 |
|
Haze |
D1003 |
% |
10 |
|
Gloss (45°) |
D2457 |
Rating |
56 |
| Application |
|---|
|
It is suitable for application in Shrink hoods, Industrial sacks, Heavy duty, carrier bags and liners |
| Packaging |
|---|
|
25 Kg plastic bag |
PRODUCT DATA SHEET
POLYETHYLENE | LLDPE | LL0209 KJ
| Product Category |
|---|
|
POPOLYMER |
| Product Name |
|---|
|
POLYETHYLENE – LLDPE |
| Grade |
|---|
|
LL0220 AA |
| Property | Test Method (ASTM) | Unit | Value |
|---|---|---|---|
|
Density |
0.92 |
g/cm3 |
ISO1183 |
|
Melt Flow Rate (190°C /2.16kg) |
2.2 |
g/10min |
ISO1133 |
|
Melting point |
|
°C |
ISO3146 |
|
Vicat softening temperature, A/50 |
93 |
°C |
ISO306 |
|
Impact Strength |
Gr |
130 |
ASTM D1709 |
|
Tear Strength TD |
G/25μ |
300 |
ASTM D1922 |
|
Tear Strength MD |
G/25μ |
110 |
ASTM D1922 |
|
Yield Stress TD |
MPa |
11 |
ISO 527 |
|
Yield Stress MD |
MPa |
10 |
ISO 527 |
|
Tensile Strength TD |
MPa |
MPa |
ISO 527 |
|
Tensile Strength MD |
MPa |
36 |
ISO 527 |
|
Elongation at break TD |
% |
800 |
ISO 527 |
|
Elongation at break MD |
% |
600 |
ISO 527 |
|
Modulus of elasticity TD |
MPa |
|
ISO 527 |
| Application |
|---|
|
It is suitable for application in Shrink hoods, Industrial sacks, Heavy duty, carrier bags and liners |
| Packaging |
|---|
|
25 Kg plastic bag |
PRODUCT DATA SHEET
POLYETHYLENE | LLDPE | LL 0220 KJ
| Product Category |
|---|
|
POLYMER |
| Product Name |
|---|
|
POLYETHYLENE – HDPELPOLY |
| Grade |
|---|
|
EX5 |
| Property | Test Method | Unit | Value |
|---|---|---|---|
|
MFI(190°C /2.16Kg) |
ASTM D 1238 |
ASTM D 1238 |
2.3 |
|
MFI(190°C /21.6Kg) |
ASTM D 1238 |
ASTM D 1238 |
– |
|
Density |
ASTM D 1505 |
Gr/cm³ |
0.92 |
|
Haze |
ASTM D 1003 |
% |
12 |
|
Gloss(45°) |
ASTM D 2457 |
% |
30 |
|
Anti-Oxidant |
|
|
√ |
|
Anti-Block |
|
|
√ |
|
Slip Agent |
|
|
√ |
|
Dart Drop Impact |
ASTM D1709(A) |
G |
90 |
|
Tear Strength MD/TD |
ASTM D 1922 |
Gr/25μm |
100/300 |
|
Tensile Strength at yield MD/TD |
ASTM D 882 |
MPa |
43019 |
|
Tensile Strength at Break MD/TD |
ASTM D 882 |
MPa |
30/25 |
|
Elongation at Break MD/TD |
ASTM D 882 |
% |
1000/1100 |
|
Secant Modulus MD/TD |
ASTM D 882 |
MPa |
80/100 |
|
Coefficient of friction |
ASTM D1894 |
– |
0.13 |
|
Vicat Softening Temperature |
ASTM D 1525 |
°C |
100 |
|
Melting Point |
BPC |
°C |
123 |
| Application |
|---|
|
Shipping sacks -Carrier and garbage bags Consumer packaging -High clarity film if
blended with LDPE.-In lean blend to producing FFS and agricultural film. |
| Packaging |
|---|
|
25 Kg plastic bag |
PRODUCT DATA SHEET
POLYETHYLENE | LLDPE | 22501
| Product Category |
|---|
|
POPOLYMER |
| Product Name |
|---|
|
POLYETHYLENE – LLDPE |
| Grade |
|---|
|
22501 |
| Property | Test Method | Unit | Value |
|---|---|---|---|
|
Density |
ASTM D 1505 |
(g/ml) |
0.922 |
|
MFR(190°C/2.16kg) |
ASTM D 1238 |
(g/10min) |
0.95 |
|
Dart Impact |
ASTM D 1709 |
(g) |
80 |
|
Elmendorf Tear MD/TD |
ASTM D 1922 |
(g) |
105/460 |
|
Tensile strength at yield MD/TD |
ASTM D 882 |
(MPa) |
13/12.5 |
|
Tensile strength at Break MD/TD |
ASTM D 882 |
(MPa) |
45/30 |
|
Ultimate Elongation MD/TD |
ASTM D 882 |
(%) |
680/780 |
|
2% Secant modulus MD/TD |
ASTM D 882 |
(MPa) |
200/240 |
|
Haze |
ASTM D 1003 |
(%) |
21 |
|
Gloss 45° |
ASTM D 245 |
(%) |
38 |
| Application |
|---|
|
Blown film grade |
| Packaging |
|---|
|
25 Kg plastic bag |